If you are going to buy discount and high-quality steel pipe ASTM A335P11 seamless ferritic alloy steel pipe for high temperature service from one ASTM A335P11 seamless ferritic alloy steel pipe for high temperature service supplier in China, or you want to check the pricelist with one of the famous A335P11 pipe, SA335P11 pipe, ASTM A335P11 pipe, ASME SA335P11 pipe, alloy steel pipe, ferritic alloy-steel pipe, alloy-steel boiler tube, high-temperature service tube manufacturers, providing with the products free sample, QIANZHOU is always at your service.
Product Description
Standards: ASTM A335/335M (ASME SA335/SA335M)
Size (mm):
Outer Dimensions: 19mm ~ 168.3mm
Wall Thickness:2.0mm ~ 14 mm
Length: max 16000mm
Port of shipment：Shanghai / Lianyungang
Application: Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service.
The main products of steel / steel grade: P11
Different chemical content:The carbon content of Gr.P11 is 0.05% to 0.15%,the silicon content is 0.5% to 1% , the chromium content is 1% to 1.5% and the molybdenum is 0.44% to 0.65%.
Machanical properties:The tensile strength of Gr.P9 is at least 415 MPa and its yield strength is at least 205 MPa.
Packing: Bare packing/bundle packing/crate packing and suitably protected for sea-worthly delivery or as requested.
Inspection and Test: Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength,Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test,No-destructive Test, Hydrostatic Test.
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
Chemical Composition (%)
C |
Mn |
P(≤) |
S(≤) |
Cr |
Mo |
Cu |
Ni |
|
P11 |
0.05-0.15 |
0.30-0.60 |
0.025 |
0.025 |
1.00-1.50 |
0.44-0.65 |
/ |
/ |
Mechanical Properties
Grade |
Yield Strength (Mpa) |
Tensile Strength (Mpa) |
Elongation (%) |
P11 |
≥205 |
≥415 |
20 |